♦ Weliding Wire Name: ErNiCrMo-3, Inconel 625 TIG/MIG Wire
♦ MOQ:15kg
♦ Form: MIG(15kgs/spool), TIG(5kgs/box)
♦ Size: Diameter 0.01mm-8.0mm
♦ Common Size:0.8MM / 1.0MM / 1.2MM / 1.6MM / 2.4MM / 3.2MM / 3.8MM / 4.0MM / 5.0MM
♦ Standards: Conforms to Certification AWS A5.14 ASME SFA A5.14
ErNiCrMo-3 used for welding 625 (N06625) alloy, 20 alloy, 825,25-6Mo,9%Ni steel or other molybdenum steel, also used for welding of different materials and corrosion resistant surfacing of material surface.
Excellent mechanical properties at high and low temperatures. Resistance to strong corrosion, stress corrosion crack, pitting and backlash corrosion in a wide range of oxidation and reduction media.
ERNiCrMo-3 Chemical Composition
C |
Al |
Si |
Mn |
Cr |
Ni |
Ti |
Fe |
S |
Cu |
Mo |
P |
Nb + Ta |
Others |
≤0.10 |
≤0.40 |
≤0.50 |
≤0.50 |
20.0 – 23.0 |
≥58.0 |
≤0.40 |
≤5.0 |
≤0.015 |
≤0.50 |
8.0 – 10.0 |
≤0.02 |
3.15 – 4.15 |
≤0.50 |
ERNiCrMo-3 Typical Welding Parameter
Diameter | Process | Volt | Amps | Shielding Gas | |
In | mm | ||||
0.035 | 0.9 | GMAW | 26-29 | 150-190 | Spray Transfer100% Argon |
0.045 | 1.2 | 28-32 | 180-220 | ||
1/16 | 1.6 | 29-33 | 200-250 | ||
1/16 | 1.6 | GTAW | 14-18 | 90-130 | 100% Argon |
3/32 | 2.4 | 15-20 | 120-175 | ||
1/8 | 3.2 | 15-20 | 150-220 |
ERNiCrMo-3 Mechanical Properties
Condition | Tensile Strength MPa (ksi) | Yield Strength MPa (ksi) | Elongation% |
AWS reauirement | 760(110) | Not specified | Not specified |
Typical results as welded | 790(115) | 590(85) | 35 |
Low iron content, can be used in the welding of nickel-chromium molybdenum alloy,
It can be used for cladding and welding of different base metals such as Ni-Cr-Mo alloy with stainless steel and carbon steel
It has good oxidation resistance and reducing environment.
The high content of molybdenum provides good stress and resistance to pitting and crevice corrosion.
ERNiCrMo-3 Application field:
It is suitable for welding of nickel-chrome-molybdenum alloy, such as Inconel625, Incoy 825, and can also be used for welding and surfacing of nickel-base alloy and stainless steel dissimilar materials. It can be used in the environment from low temperature to 540℃.