Mumetal SuPermalloy (1J85) sheet/STRIP/ bar/Ring
Common Trade Names: Mumetal,UNS N14080, HY-MU80,Permalloy 80, 1J79, 79НМ,
Mumetal /Permalloy 80 is a highly magnetic nickel-molybdenum-iron alloy. with roughly 80% nickel and 15% iron and 5% molybdenum content. It's useful as a magnetic core material in electrical and electronic equipment. Permalloy 80 provides high initial and maximum permeabilities with low coercive force, low hysteresis loss, low eddy-current losses, and low magnetostriction which is critical for industrial applications.
Applications:
• Transformer laminations • Relay • Recording Heads •Deflection and Focusing Yokes • Amplifiers •Loudspeakers •Shielding.
|
Grade |
U.K. |
Germany |
U.S.A. |
Russia |
Standard |
|
Mumetal (1J79) |
Mumetal |
/ |
Permalloy 80 HY-MU80 |
79HM |
ASTM A753-78 GBn 198-1988 |
Mumetal Chemical Composition
| Grade |
Chemical Composition (%) |
||||||||
| C | P | S | Cu | Mn | Si | Ni | Mo | Fe | |
| Mumetal 1J79 | ≤ | ||||||||
| 0.03 | 0.020 | 0.020 | 0.20 | 0.60~1.1 | 0.30~0.50 | 78.5~80.0 | 3.80~4.10 | Balance | |
Mumetal Physical Property
|
Grade |
Resistivity (μΩ•m) |
Density (g/cm3) |
Curie point °C |
saturation magnetostriction constant (×10-2) |
Tensile Strength/MPa |
Yelid Strength/MPa |
||
|
Mumetal 1J79 |
Unannealed |
Annealed |
Unannealed |
Annealed |
||||
|
0.40 |
8.20 |
980 |
2 |
1030 |
560 |
980 |
150 |
|
Mumetal Avager Linear Expansion
|
Grade |
Coefficient of Linear Expansion at Different Temperaturel(x 10-6/K) |
||||||||
|
20～100℃ |
20～ 200℃ |
20～ 300℃ |
20～400℃ |
20～ 500℃ |
20～ 600℃ |
20～ 700℃ |
20～ 800℃ |
20～ 900℃ |
|
|
Mumetal 1J79 |
10.3-10.8 |
10.9～ 11.2 |
11.4～ 12.9 |
11.9～ 12.5 |
12.3～ 13.2 |
12.7～ 13.4 |
13.1～ 13.6 |
13.4～ 13.6 |
13.2～ 13.7 |
Mumetal Shielding Potential
Permalloy has extremely high permeability and nominal coercive force that make it a suitable material for shielding operations. To achieve the desired shielding properties, HyMu 80 is annealed up to 1900oF or 1040oC subsequent to forming processes. Annealing at the elevated temperatures enhances the permeability and shielding properties.