Stainless Steel Alloy PH13-8Mo(13-8PH)
Common Trade Names: 13-8Mo, PH13-8Mo, S51380, 04Cr13Ni8Mo2Al, xm-13,UNS S13800,Werkstoff 1.4548
PH13-8Mo stainless is a martensitic precipitation hardening stainless steel that has excellent strength, high hardness, superior toughness and good corrosion resistance. Good transverse toughness properties are achieved by tight chemical composition control, low carbon content, and vacuum melting. Typical applications are large airframe structural components and injection molding equipment.
|
C |
Cr |
Ni |
Mo |
Si |
Mn |
P |
S |
Al |
N |
Fe |
|
≤ 0.05 |
12.25 13.25 |
7.5 8.5 |
2.0 2.5 |
≤ 0.1 |
≤ 0.2 |
≤ 0.01 |
≤ 0.008 |
0.9 1.35 |
≤ 0.01 |
Bal |
|
Density |
Melting point |
|
7.76 |
1404-1471 |
Strength varies with heat treatment condition. The following table shows minimum mechanical properties for the various aged conditions, per AMS 5864
| H950 | H1000 | H1025 | H1050 | H1100 | H1150 | |
| 0.2 Offset Yield Strength, ksi | 205 | 190 | 175 | 165 | 135 | 90 |
| Ultimate Tensile Strength, ksi | 220 | 205 | 185 | 175 | 150 | 135 |
| Elongation in 2", % | 10 | 10 | 11 | 12 | 14 | 14 |
| Reduction of Area, % (Longitudinal) | 45 | 50 | 50 | 50 | 50 | 50 |
| Reduction of Area, % (Transverse) | 45 | 50 | 50 | 50 | 50 | 50 |
| Reduction of Area, % (Short-Transverse) | 35 | 40 | 45 | 45 | 50 | 50 |
| Min Hardness, Rockwell | 45 | 43 | - | 40 | 34 | 30 |
PH 13-8Mo Standards and Specifications
AMS 5629,ASTM A 564,EN 1.4548,UNS S13800,Werkstoff 1.4548
PH 13-8Mo Available Products in Sekonic Metals
PH 13-8Mo Bars & Rods
Round bars/Flat bars/Hex bars, Size From 8.0mm-320mm, Used for bolts,fastners and other spare parts
PH 13-8Mo sheet & plate
Widths up to 1500mm and lengths up to 6000mm,Thickness from 0.1mm to 100mm.
PH 13-8Mo strip & coil
Soft condition and hard condition with AB bright surface, width up to 1000mm
Why PH13-8Mo ?
• High strength, good fracture toughness, transverse mechanical properties and stress corrosion resistance in Marine environment.
• Weldability：By an inert gas protection welding, also using most of the other welding process, including plasma welding, electron beam welding, And argon shielding gas is preferred.
PH13-8Mo Application field：
Widely used in aerospace, nuclear reactors and petrochemical and other fields, such as cold heading fasteners and
machining, aircraft components, reactor components and petrochemical equipment.