Stainless steel 17-7PH
Common Trade Names: 17-7PH,SUS631,S17700,07Cr17Ni7Al,W.Nr.1.4568
17-7PH is austenitic-martensitic precipitation hardening stainless steel developed on the basis of 18-8CrNi, also known as controlled phase change stainless steel.At the solution treating temperature, 1900°F, the metal is austenitic but undergoes transformation to a low-carbon martensitic structure during cooling to room temperature. This transformation is not complete until the temperature drops to 90°F. Subsequent heating to temperatures of 900-1150°F for one to four hours precipitation strengthens the alloy. This hardening treatment also tempers the martensitic structure, increasing ductility and toughness
| C | Cr | Ni | Si | Mn | P | S | Al |
| ≤0.09 | 16.0-18.0 | 6.5-7.75 | ≤1.0 | ≤1.0 | ≤0.04 | ≤0.03 | 0.75-1.5 |
| Density (g/cm3) | Melting point（℃） |
| 7.65 | 1415-1450 |
| Condition | бb/N/mm2 | б0.2/N/mm2 | δ5/% | ψ | HRW | |
| Solution treatment | ≤1030 | ≤380 | 20 | － | ≤229 | |
| Precipitationhardening | 510℃ageing | 1230 | 1030 | 4 | 10 | ≥383 |
| 565℃ageing | 1140 | 960 | 5 | 25 | ≥363 | |
17-7PH Standards and Specifications
AMS 5604, AMS 5643, AMS 5825,ASME SA 564, ASME SA 693, ASME SA 705, ASME Type 630,ASTM A 564, ASTM A 693, ASTM A 705, ASTM Type 630
Condition A - H1150,ISO 15156-3,NACE MR0175,S17400,UNS S17400,W. Nr./EN 1.4548
| Bar/Rod | Wire | Strip/Coil | Sheet/Plate | Pipe/Tube |
17-7PH Available Products in Sekonic Metals
17-7PH Bars & Rods
Round bars/Flat bars/Hex bars, Size From 8.0mm-320mm, Used for bolts,fastners and other spare parts
17-7PH Wire
Supply in welding wire and spring wire in coil form and cut length.
17-7PH sheet & plate
Widths up to 1500mm and lengths up to 6000mm,Thickness from 0.1mm to 100mm.
17-7PH seamless tube & Welded pipe
Standards size and customized dimension can be produced by us with small tolerance
17-7PH strip & coil
Soft condition and hard condition with AB bright surface, width up to 1000mm
17-7PH Fasteners
17-7PH materials in forms of Bolts,screws,flanges and other fasterners, according to clients specification.
Why 17-7 PH?
• High tensile strength and hardness to 600°F
• Corrosion resistant
• Excellent oxidation resistance to about 1100°F
• Creep-rupture strength to 900°F
17-7 PHApplication field：
• Gate valves
• Chemical processing equipment
• Pump shafts, gears, plungers
• Valve stems, balls, bushings, seats
• Fasteners